热处理工艺对6063铝合金强度和导电率的影响热处理工艺对6063铝合金强度和导电率的影响颜建辉1,陈辉煌2(1.湖南科技大学材料表面工程研究所,湖南湘潭411201;2.南方冶金学院材料与化学工程分院,江西赣州341010)摘要:研究了热处理工艺参数(如时效温度、时间等)对6063铝合金的强度和导电率的影响。结果表明,低温长时间和高温短时间都可以提高强度,而随着时效温度的提高和时效时间的延长,6063铝合金的导电率呈上升趋势。关键词:6063铝合金;热处理工艺;强度;导电率中图分类号:TG146.2+1;TG156.92文献标识码:A文章编号:101123814(2004)022*******EffectoftheHeatTreatmentontheStrengthenandElectricalConductivityof6063AluminumAlloyYANJian2hui1,CHENHui2huang2(1.InstituteofMaterialSurfaceEngineering,HunanUniversityofScienceandTechnocogy411201,China;2.CollegeofMater.andChem.Eng.,SouthernMetallurgyInstitute,Ganzhou341010,China)Abstract:Theeffectofthetemperatureandtimeoftheagingheattreatmentonthestrengthenandtheelectricalconductivityof6063aluminumalloyhavebeenstudied.Theresultsshowthatthestrengthencanbeimprovedbylowtemperaturebutlongagingtimeorhightemperaturebutshortagingtime.Theelectricalconductivityincreasesasthetemperatureorthetimeoftheagingheatisincreased.Keywords:6063Aluminumalloy;heattreatmenttechnology;strengthen;electricalconductivityΞ6063铝合金以其中等强度,良好的抗腐蚀性、抛光性、阳极氧化着色性及涂漆性能,在装饰性结构中得到广泛应用。同时,因其具有良好的导电、导热性能,也广泛用作电脑CPU的散热片。6063铝合金的性能除了与化学成分有关外,还与热处理工艺有关。为了兼顾各种性能,本文结合合金的化学成分,着重研究了其时效机制及对力学性能和导电率的影响。1实验方法实验用材的化学成分见表1。材料是铸锭经490℃均热后,于480℃挤成型材经风冷淬火,再矫直后获得的电脑散热片型材。电阻测定按[JIS1967]《有色金属材料的体积电阻率和导电率的测试方法》进行。表1实验用6063铝合金化学成分(质量分数,%)合金SiMgFeCuMnZnCrTi余量A0.320.510.150.000.000.000.000.02AlB0.380.500.220.0350.000.000.000.03AlC0.450.500.250.0460.010.010.010.04Al实验采用的不同的时效制度分别是:(1)自然时效:2、10、30、120、730、1440h;(2)175℃时效:1、2、4、6、8、12h;(3)200℃时效:1、2、3、4、6、9h;(4)235℃时效:1、2、3、4、6、9h。2实验结果2.1时效对强度的影响图1可知,自然时效后3种合金型材的抗拉强度以大致相同的速率提高,经1440h自然时效后,强度图1时效对6063铝合金力学性能影响的特性曲线约增加20%～40%,大部分的强度值增加在第一天,而后增加速率下降。175℃时效,在开始的1～7h阶段时,强度增加的速率较大,然后增加的很缓慢;而200℃时效时,时效初期强度上升幅度很大,到约2h后趋缓,约4h时达到峰值,其后随时间的延长,强度开始下降而进入过时效阶段,然后开始逐渐减小;235℃时效时,在开始的1h左右,强度是最大的,然后随着时效时间延长,强度开始逐渐减小。在同一时效制度中,由于3种合金的成分不同,C合金强度最大,B合金次之,最小的是A合金。这是由于杂质Fe和Zn94《热加工工艺》2004年第2期工艺技术Ξ收稿日期:2003207320作者简介:颜建辉(19732),男,江西莲花人,硕士。本文来源：网络收集与整理，如有侵权，请联系作者删除，谢谢！