临床医学论文•多孔明胶微球/磷酸钙骨水泥的制备及其性能硏究作者：厉孟，刘旭东，刘兴炎，葛宝丰【摘要】［冃的］制备多孔明胶微球/磷酸钙骨水泥，并于体内体外硏究其各种性能。［方法］双相乳化冷凝聚合法制备明胶微球，以不同比例与磷酸钙骨水泥复合(0%，2.5%，5%)，制备多孔磷酸钙骨水泥，测定材料孔径率及抗压强度，筛选出最佳比例。消化法培养成骨细胞接种于常规及多孔磷酸钙骨水泥支架上，扫描电镜观察细胞形态;不同材料浸提液(0%，2.5%明胶微球/磷酸钙骨水泥及聚苯乙烯)分别与成骨细胞共培养，以MTT法测定细胞增殖率，试剂盒检测碱性磷酸酶水平。将磷酸钙骨水泥及2.5%明胶微球/磷酸钙骨水泥分别植入山羊椎体内,6个月后收集标本，分别进行X线影像学及组织学观察，评估其降解情况。［结果］不同比例明胶微球/磷酸钙骨水泥的总孔径率、大孔率及抗压强度分别为38.7%、0%、12.1MPa(0%);67.5%'40.6%、8.0MPa(2.5%);72.2%'45.6%、5.0MPa(5%)。成骨细胞在明胶微球/磷酸钙骨水泥上生长良好，细胞增殖及碱性磷酸酶水平均明显高于单纯磷酸钙骨水泥组，勻聚苯乙烯组未见明显差异。多孔明胶微球/磷酸钙骨水泥6个月后在体内大部分已降解，而磷酸钙骨水泥未见明显降解。［结论］复合明胶微球可显著提高磷酸钙骨水泥的孔径率促进其降解，增加其生物活性，这种多孔磷酸钙骨水泥可作为非负重部位的骨替代物。【关键词】多孔磷酸钙骨水泥；明胶微球；孔径率；抗压强度；骨替代物---本文来源于网络，仅供参考，勿照抄，如有侵权请联系删除---Abstract:[ObjcctiveJTodevelopmacroporouscalciumphosphatecements(CPCs)byincorporatingthegelatinmicrospheres(GMs)andtoevaluatetheperformanceofthecompositeasabonesubstituteinvitroandinvivo.[Mcthods]GMswerepreparedbyimprovedemulsifiedcold・condcnsnlionmethodandmacroporousCPCsweredevelopedusingGMswiththreedifferentweightratios(0%,2.5%and5%)・TheporosityandthecompressionstrengthofthethreecompositesweremeasuredtodeterminetheproperweightratioofGMs.ThemorphologicchangesofosteoblastswereexaminedwithscanningelectronmicroscopeattwodaysafterthecelIswereseededontheCPCsandGMs/CPCs.ThecelIswerealsoculturedwithdifferentleachingliquorofthreekindsofmaterials(0%,2.5%GMs/CPCsandpolystyrene).Cel1viabilityanalysiswasperformedbyMTTassay,andalkalinephosphatasewasmeasuredwithalkalinephosphatasekit.Atsixmonthsafterimplantedinthegoatvertebre,thesampleswithCPCsorGMs/CPCswereobtainedandevaluatedbyX・rayimageandhistologicalanatomy.[Results]PorosityoftheGMs/CPCsincreasedwiththeincreaseofGMs,butcompressionstrengthdecreased.Theproliferationanddifferentiationoftheosteoblastswereenhancedwiththe2.5%GMs/CPCscomparedtotheCPCs.InvivostudyshowedthatthedegradationofGMs/CPCswasimproved・[Cone1usion]Macroporouscalciumphosphatecementscanbedevelopedbyincorporatinggelatinmicrospheres,andbiocompatibi1ityanddegradabi1ityofthecompositecanbeenhanced.Thecompositecanbeusedasabonesubstituteundernon-loadedcircumstances.---本文来源于网络，仅供参考，勿照抄，如有侵权请联系删除---Keywords:calciumphosphatecements;gelatinmicrosphere;porosity;compressivestrength;bonesubstitute随着各种创伤造成的骨缺损病例日益增加，对修复材料的需求也与口俱增。自体骨被奉为修复骨缺损的金标准，但来源有限，异体骨效果也较好，但存在伦理及疾病传播的问题。磷酸钙骨水泥（calciumphosphatecements,CPCs）作为新型的骨修复材料，具有可注射、塑形好、骨传导性强等优点，但较慢的吸收率阻碍了其广泛应用;增加孔径率可明显加速CPCs的吸收，是目前CPCs改性硏究的热点[1'2]°本硏究通过复合明胶微球（gelatinmicrospheres,GMs）来制备多孔CPCs，并对其体外生物活性及体内降解率进行了一系列的硏究。1材料及方法1.1主要设备与试剂78HW-1型恒温磁力搅拌...