高纯六水氯化锶的制备工艺研究高纯六水氯化锶的制备工艺研究程忠俭,常玉普,王连毅(河北辛集化工集团有限责任公司,河北辛集052360)摘要:从反应原理出发,以工业碳酸锶或次锶为原料,经过工业盐酸酸化、净化,除去钡、铁及其他杂质,然后蒸发、浓缩、结晶、过滤、烘干,制得高纯六水氯化锶。通过实验得到最佳的除钡和除铁工艺参数,分析了结晶浓度对晶形的影响,并确定了结晶的工艺参数及所得成品的烘干温度。通过以上方式制得的高纯六水化化锶产品纯度高、晶型好,对实际生产具有很好的指导意义。关键词:高纯六水氯化锶;碳酸锶;结晶中图分类号:TQ132.33文献标识码:A文章编号:1016-41010(2022)11-0046-02StudyonproductiontechnologyofhighpuritystrontiumchloridehexahydrateChengZhongjian,ChangYupu,WangLianyi(HebeiXinjiChemicalGroupCo.,Ltd.,Xinji052360,China)Abstract:Startingfromtheprincipleofreaction,industrialstrontiumcarbonateorlow-gradestrontiumwasusedasrawmaterialandhighpuritystrontiumchloridehexahydratewaspreparedthroughacidificationbyindustrialhydrochloricacid,removalofbarium,iron,andotherimpurities,andthenevaporation,concentration,crystallization,filtering,anddrying.Throughtheexperiment,theoptimumparametersofremovingbariumandironwereobtained.Impactofcrystalconcentrationonthecrystalphasewasanalyzedandthecrystallizationprocessparametersanddryingtemperatureforfinishedproductweredetermined.Productsbasedontheabovetechnologyhadahighpurityandgoodcrystalphase,andthereforethetechnologyisagoodguidanceforthepracticalproduction.Keywords:highpuritystrontiumchloridehexahydrate;strontiumcarbonate;crystallization高纯六水氯化锶可用于制造高档磁性材料、电解金属钠的助熔剂、高档颜料和液晶玻璃,也可用于制药工业和日用化工,制造其他高纯锶盐如高纯碳酸锶等,具有很高的经济价值。笔者采用成本相对较低的碳酸锶盐酸法,以工业碳酸锶或次锶为原料,经工业盐酸酸化、净化除钡、铁及其他杂质,然后蒸发、浓缩、结晶、过滤、烘干,制得高纯六水氯化锶。1实验1.1原料工业碳酸锶[质量分数为101.32%,w(Ba)=1.06%,w(Fe)=2.410-5]、工业盐酸(质量浓度为344.3g/L)、工业硫酸(浓度为1mol/L)、氢氧化锶等。1.2实验过程将纯水(或氯化锶母液)加入烧杯内,搅拌下加入适量碳酸锶粉末,制成浆料,缓慢加入工业盐酸进行酸化,然后喷淋加入适量的硫酸,再加入质量分数为30%的双氧水少许,用氢氧化锶调节pH至8~10,加热至60~70,搅拌1h,过滤,除去残渣,滤液加热至沸,继续浓缩至氯化锶质量浓度为650~670g/L,然后缓慢降温,控制降温速度10/h,以达到控制晶体成长速度的目的。冷却至35以下,滤出结晶,结晶用少量常温氯化锶饱和溶液淋洗,抽滤,用50~60热风吹干。1.3实验结果及产品质量以工业碳酸锶和工业盐酸为原料,进行复分解反应,经除杂、结晶、烘干后,得高纯六水氯化锶成品。所得产品主含量大于101.0%(质量分数,下同),w(硫酸根)<510-5,w(钡)<510-5,w(钙)<510-5,w(铁)<510-6,w(镁)<210-6,w(重金属)<110-6,w(水不溶物)<0.005%,大部分指标满足分析纯六水氯化锶的要求,全部指标达到化学纯六水氯化锶的要求。46无机盐工业INORGANICCHEMICALSINDUSTRY第42卷第11期2022年11月本文来源：网络收集与整理，如有侵权，请联系作者删除，谢谢！